Three Standards For Mold Selection Materials

Hello, come to consult our products !

(1)Corrosion resistance

When some molds such as plastic molds are working, due to the presence of chlorine, fluorine and other elements in the plastics, strong corrosive gases such as hci and hf will be resolved after being heated, which will erode the surface of the mold cavity, increase its surface roughness, and aggravate wear failure.

(2) The mold meets the process performance requirements

The manufacturing of molds generally involves several processes such as forging, cutting, and heat treatment. In order to ensure the manufacturing quality of the mold and reduce the production cost, the material should have good forgeability, machinability, hardenability, hardenability and grindability; it should also have small oxidation, decarburization sensitivity and quenching Deformation and cracking tendency.

1. Forgeability
It has low hot forging deformation resistance, good plasticity, wide forging temperature range, low tendency of forging cracking and cold cracking and precipitation of networked carbides.
2. Annealing processability
The spheroidizing annealing temperature range is wide, the annealing hardness is low, the fluctuation range is small, and the spheroidizing rate is high.
3. Machinability
The cutting amount is large, the tool loss is low, and the machined surface roughness is low.
4. Sensitivity to oxidation and decarburization
When heated at high temperature, the oxidation resistance is good, the decarburization speed is slow, the heating medium is not sensitive, and the tendency of pitting is small.
5. Hardenability
After quenching, it has uniform and high surface hardness.
6. Hardenability
After quenching, a deeper hardened layer can be obtained, and it can be hardened by using a mild quenching medium.
7. Tendency of quenching deformation and cracking
Conventional quenching has small volume change, shape warping, slight distortion, and low tendency of abnormal deformation. Conventional quenching has low sensitivity to cracking, and is insensitive to quenching temperature and workpiece shape.
8. Grindability
The grinding wheel is relatively low in wear, and the non-burn limit grinding consumption is large. It is not sensitive to the quality of the grinding wheel and cooling conditions, and it is not easy to cause abrasion and grinding cracks.


Post time: Dec-28-2020